Properties Dielectric constant Chemical durability
Transcription
Properties Dielectric constant Chemical durability
AGC's aluminosilicate glass for chemical strengthening Properties Properties Dragontrail Sodalime Density [g/cm3] 2.48 2.50 g [ ] Young's Modulus [GPa] 74 73 Shear Modulus [GPa] 30 30 Poisson’s Ratio 0.23 0.21 Vickers hardness (before CS) 595 533 Vickers hardness (after CS) 673 580 ‐7 ( g )) [deg.] [ g] CTE(50‐350deg.x10 98 85 Tg [deg.] 604 550 Softening Point [deg.] 831 733 Annealing Point [deg.] 606 554 Strain Point [deg.] 556 511 ( ) Refraction Index (Nd) 1.51 1.52 Photoelastic constant [nm/cm MPa] 28.3 25.6 Volume Resistivity [Ω・cm] 8.4 8.5 Mechanical property Thermal property Optical property Electrical property Dielectric constant Frequency Dielectric constant [Hz] Chemical durability Loss tangent 1M 7.3 0.032 10M 7.3 0.032 54M 7.1 0.028 490M 7.0 0.029 912M 7.0 0.030 Chemical reagent HCL NaOH HF BHF 0.1mol/l for 20hrs. 0.1mol/l 90o for 20hrs. 5% 25o for 20min. for 20min 1:9 25o for 20min. 90o Etching amount Weight loss h l h [mg/cm2] [um/cm2] 0.03 0.01 0.56 0.14 11.76 2.92 0.98 0.24 AGC's aluminosilicate glass for chemical strengthening 90 80 70 Chemical strengthening capability p y DO OL [um] 60 50 Dragontrail 40 30 20 Sodalime 10 0 450 Transmittance of Dragontrail (0.7mmt) Transmitttance[%] 95 90 85 80 75 70 200 400 600 800 1000 1200 1400 1600 500 Cumulative fractu ure probability ratio 400 550 600 650 700 CS [MPa] 750 800 850 Bending strength 2.0 1.0 Dragontrail Sodalime 0.0 ‐1 1.0 0 ‐2.0 ‐3.0 ‐4.0 Failure Stress[MPa] Wavelength[nm] Scratch visibility Sodalime Dragontrail Asahi Glass Co., Ltd. AGC Electronics 1‐5‐1, Marunouchi, Chiyoda‐ku, Tokyo 100 8405 JAPAN Tokyo 100‐8405 JAPAN Scratched by diamond tip Tip size: R=50um Scratching speed: 2mm/sec Copyright(c) Asahi Glass Co., Ltd. All rights reserved 900