Export gb+f

RP
Brand:
Appellation:
WS.- No.:
WS.- No.:
DIN standards:
Symbole DIN:
Typical analysis %:
Analyse moyenne %:
RP
1.2365
32CrMoV12-28
C
Si
0,32 0,4
Mn
0,4
Cr
3,0
Mo
2,8
V
0,6
Type of steel and characteristics:
Tempering diagram 60 Ø, 1030°C oil
Courbe de revenu 60 Ø, 1030°C huile
Chromium moybdenum vanadium hot work steel. Very good high temperature
strength and tempering resistance. Water cooling possible owing to good
conductivity. Suitable also for cold hobbing with special heat treatment.
Applications:
Extrusion tools for aluminium, copper alloys and steel, such as dies and inserts,
dummy blocks, die holders and mandrels; die casting tools for aluminium and
copper alloys; die forging tools for copper alloys; tools for making bolts and nuts;
die-inserts, punches, jaws etc. used on forging presses; piercing and other tools
on push benches for steel tube production.
Heat treatment:
Annealing:
Dureté HRC
Hardness after annealing:
Stress relieving:
Hardness HRC
Hardening:
Hardness obtainable:
Tempering:
Tempering temperature °C
Nitriding:
Preheating before use:
Température de revenu en °C
Diagram of high temperature strength 30 Ø
Résistance à chaud 30 Ø
reduction of area %
0,2- proof stress and tensile strength N/mm2
Limite élastique 0,2 et résistance à la traction N/mm2
striction %
Type d’acier et caractéristiques:
Acier pour le travail à chaud, à base de CrMoV, sans tungstène. Excellente tenue
au revenu et résistance à chaud; insensible aux chocs thermiques grâce à une
bonne conductibilité, donc refroidissable à l’eau. En outre cet acier se prête à
l’enfonçage à froid.
Utilisations:
Outils pour le filage de l’acier et des alliages cuivreux, tels que filières, aiguilles,
disques presseurs, porte-filières, âmes de conteneurs; outillages de coulée sous
pression des alliages légers; outillages pour la coulée sous pression des alliages
cuivreux en cas de fortes épaisseurs; outils de matriçage des alliages cuivreux;
poinçons, matrices et éjecteurs pour la boulonnerie; outillages pour presses à
forger; outils de bancs de poussée pour tubes acier.
Traitement thermique:
Recuit d’adoucissement:
Dureté après recuit:
Recuit de détente:
Trempe:
test temperature °C
température de contrôle °C
Dureté après trempe:
Revenu:
Nitruration:
Préchauffage:
40
Temperature: 820 - 840°C
Holding time: 4- 6 h; Slow furnace cooling
max. 220 HB (175 HB for hobbing).
Temperature: appr. 650°C
Holding time: 2-4 h; Slow cooling
Temperature: 1020 - 1050°C
Quenching: oil or polymer, or hot bath at appr.
540°C, (when oil or polymer, interrupt at
230 - 280°C), or vacuum hardening.
appr. 51 HRC (oil or polymer quenching)
Temperature: 580 - 700°C see diagram.
To increase toughness, temper 2 or 3 times.
possible.
250 - 350°C – absolutely necessary.
Température: 820 - 840°C
Durée: 4 à 6 h; Refroidissement lent au four
max. 220 HB (175 HB p. enfonçage à froid)
Température: env. 650°C
Durée: 2 à 4 h; Refroidissement lent
Température: 1020 - 1050°C,
Refroidissement: huile ou polymer, ou bain chaud
de 540°C (huile ou polymer: interrompre à
env. 230 - 280°C); ou sous vide.
env. 51 HRC (à l’huile ou polymer).
Température: 580 - 700°C, v. diagramme.
Pour augmenter la tenacité, effectuer 2 à 3 revenus.
possible.
250 - 350°C, nécessaire, avant mise en service.